Synthesis of nanosized TiO2 powder by sol gel method at low temperature

Abstract : Nanotechnology is all about making products from very small constituents, components or subsystems to gain greatly enhanced material properties and functionality. Nanocrystalline anatase TiO2 was prepared by a facile sol–gel route at a temperature of 50°C under mild conditions. Titanium tetraisopropoxide (TTIP) was used as a titanium precursor, and 2-propanol was used as a solvent. XRD, TEM, SEM, FT-IR and BET were applied to characterize the crystal phase. The Crystalline size of TiO2 powder has been obtained with diameter < 30 nm for anatase at 500°C using an acid.
Document type :
Journal articles
Complete list of metadata
Contributor : Julie Cagniard Connect in order to contact the contributor
Submitted on : Monday, January 25, 2021 - 2:57:00 PM
Last modification on : Wednesday, November 3, 2021 - 9:11:49 AM




W. Nachit, Samira Touhtouh, Z. Ramzi, Mohamed Zbair, Adil Eddiai, et al.. Synthesis of nanosized TiO2 powder by sol gel method at low temperature. Molecular Crystals and Liquid Crystals, Taylor & Francis, 2016, 627 (1), pp.170-175. ⟨10.1080/15421406.2015.1137135⟩. ⟨hal-03120411⟩



Record views